7 Common Defects with Injection Moulding and How to Avoid Them

Learn more about common injection moulding defects and how to redesign your parts to avoid them.

7 Common Defects with Injection Moulding and How to Avoid Them

With its ability to produce a high volume of plastic parts inexpensively, Injection Moulding is often a common manufacturing solution for many engineers. However, without proper attention to the design of components, there are risks associated with the process.

Injection Moulding can occasionally produce results with defects. Some types of defects are more serious than others, and the prevalence of defects does depend on the nature of the part and the type of plastic used. However, by paying close attention to the design of components, there are ways in which designers and machine operators can avoid and reduce the effects of defects.

Read our guide below to learn of common defects with Injection Moulding and, more importantly, how to avoid them.

{{cta-banner}}

Flow lines

Flow lines are streaks or patterns that are off toned in colour. They may also appear as ring-shaped bands on the plastic product’s surface, commonly near the gate (the entry point of the molten plastic into the mould).

Flow lines may be acceptable for some parts that are not visible to the consumer. However, flow lines can be unsightly and often unacceptable, especially if the final product has high aesthetic standards. The flow lines patterns are often unpredictable and can stand out due to their colour differentiation.

Flow lines are caused due to the varying cooling rates and flow velocities within the molten plastic flowing through the mould. These variations in plastic flow create small bands of molten plastic, which later solidify. Often moulds with complicated designs will see the molten plastic change direction due to contours and bends inside the injection moulding tool. As the plastic passes through these sections with varying speeds, occasionally, the plastic will cool too quickly. Varying wall thicknesses can be another cause of flow marks, with the plastic solidifying at varying rates.

There are several ways flow marks can be avoided, including:

  • Increasing the speed and pressure of injection, thus helping to maximise uniform filling and cooling of all cavities simultaneously.
  • Redesigning the mould to avoid sudden flow direction changes.
  • Redesigning the gate location / increasing the gate cross-section area.
  • Increasing the temperature of the molten plastic, ensuring that the plastic stays at a higher temperature when filling the mould.
  • Increasing nozzle diameter & temperature.
  • Increase mould pressure.
injection moulding flow lines

Burn Marks

Burn marks are discolouration in the final plastic product, on the surface or edge. They are usually rust or dark brown in colour.

Widely speaking, burn marks in injection moulding do not affect the part integrity; however, they can lessen the quality of the finished product aesthetically speaking.

The usual causes of burn marks are due to trapped air or the plastic becoming overheating in the heated barrel or nozzle, which in turn causes burn marks in the final part.

Preventative methods include:

  • Lowering the overall temperature of the melting stage to prevent overheating completely.
  • Reducing the resin injection speed, as this limits the risk of air becoming trapped inside the mould.
  • Enlarging the gas vents & gates as this allows trapped air to escape the mould.
  • Shortening the overall mould cycle time so that the trapped air or resin doesn’t have time to overheat.
  • Optimise the venting and degassing system.

Warping

Warping is the name given to the deformation in injection moulded products.

As molten plastic cools, the plastic contracts and reduces in size. As different areas of the mould cool at different rates, the plastic can shrink unevenly, causing variations in stress within the cooled part.

This stress results in bending and twisting of the finished part as it cools. For example, a flat part that has warped will no longer be flat. The problem is exacerbated when the plastic cools too quickly. Excessive temperatures and low thermal conductivity of the molten material can also worsen the problem considerably. Other causes of mould design warping can include irregular wall thickness, which can cause variations in cooling rates.

How to prevent warping in injection moulding

  • Always aim to ensure that the cooling process is gradual and long enough to avoid uneven stresses on the material.
  • Lowering the temperature of the material or mould is another way you can prevent warping, to prevent such rapid temperature change.
  • Another option is to switch the material you’re using, choosing a polymer that shrinks less during cooling. This may be particle-filled thermoplastics or semi-crystalline materials.
  • Redesigning the mould is another solution to ensure maximum wall thickness and part symmetry. The more symmetrical the part, the greater stability during cooling.

Surface delamination

Surface delamination in injection moulding occurs when thin layers on the polymer surface easily separate or peel off. This is called delamination and is characterised by a flaking surface layer.

Surface delamination is a serious injection moulding defect, as it affects the strength of the final component, weakening it significantly.

The common cause is, in fact, contamination of resin pellets or other base materials in the molten plastic mix. This foreign material does not bond with the original plastic material used in the mould. The two types are incompatible, causing this defect. Another cause is excess moisture or improper drying of the plastic.

There are several ways to prevent surface delamination, including;

  • Increasing the mould temperature.
  • Pre drying the material properly, as this removes any excess moisture.
  • Ensure workers store and handle the plastic with the utmost care, avoiding cross-contamination of different polymers.
  • Redesigning the mould with a focus on the injection nozzle limits the dependence on the release agents.
  • Smooth the corners and turns in the mould design, as this reduces the sharp changes of direction for the flow of the mould.
  • Focus on the ejection mechanism in the mould design, as this reduces the dependence on mould release agents, which can cause contamination.

Short shots

During the injection moulding process, molten plastic material occasionally does not fill the whole mould. If the mould cavity is not full, then the final product will have defects and be incomplete after it cools and solidifies. This process is called ‘short shot’- it is a pivotal defect, which seriously impacts the functionality of the finished product.

What are the main causes?

One of the main causes is blocked passages in the mechanism or a defect with the gate. Short shots occur if the gates narrow, if the material is too viscous, or additionally if the mould isn’t the right temperature.

Trapped air can be another cause of short shots, as the trapped air bubbles in the material affect the flow of the molten plastic.

Another potential cause for short shots is insufficient pressure during the injection of the material.

How to prevent short shots

  • Consider redesigning the mould. The molten plastic will have better flow through the mould design with wider gates or channels.
  • Increase the pressure of injection or speed of injection to ensure a more efficient flow before the material solidifies in the mould.
  • Choose a less viscous plastic.
  • Add more vents to the mould, allowing any trapped air to escape.
injection moulding short shot with mold
injection moulding short shot

Sink Marks

Sink marks are small depressions or dents in an otherwise flat surface of an injected moulded part. Sink marks are often caused by overly thick wall sections, where the molten plastic at the inside of the section pulls material inward as it cools at a slower rate, causing a noticeable defect. Sink marks can be particularly detrimental to high-quality products where an impeccable finish is required.

Sink marks are mainly caused when molten plastic cools too slowly. This is unlike other defects, which are more common due to the plastic cooling too fast. Sink marks are caused by material that takes too long to cool; the resulting shrinkage pulls materials inwards before it has cooled to form the final shape.

Sink marks are more likely to appear in thicker parts of a component.

How to avoid sink marks

  • By increasing the holding pressure & time to allow the material near the parts’ surface to cool
  • Increasing the cooling time, which limits shrinkage
  • Designing the mould with thinner walls, allowing for a faster cooling near the surface
injection moulding sink marks
injection moulding sink marks redesigned

Jetting

Jetting is a deformation within a moulded component when a jet of molten material solidifies before the cavity is full. This initial jet sets before the rest of the molten plastic have had time to solidify.

Aesthetically, jetting appears as a squiggly line on the surface of the injected mould. The line will usually start from the initial gate of injection. This visible flow pattern can also cause substantial weaknesses.

One of the main causes of jetting is excessive injection pressure. When the molten resin is injected through a small nozzle at extremely high pressure, the liquid will enter rapidly through the gate rather than filling the cavity gradually and evenly. Jetting can also occur when the melt temperature is too low, as the viscosity of the molten plastic becomes too high, increasing the resistance through the nozzle.

This initial plastic jet cools against the mould walls, solidifying as the remaining resin pushes into the mould. This action leaves impressions on the surface of the finished part.

How to prevent jetting

  • Reduce the injection pressure considerably to ensure the even injection of the material into the mould.
  • Increase the melt and mould temperatures to prevent the initial material from solidifying too early.
  • Position the gate(s) optimally, so that the material will fill the whole mould when injected.
  • Increase the gate size to increase material flow.

For more information about Get It Made’s range of services, click here. Head to our technical toolbox for industry insights. Want to learn more? Give us a call on +44 020 3286 6002 or arrange a 24-hour quote.

CNC Milling.
CNC Turning.
Plastic Injection Moulding.
Custom Aluminium Extrusion.
Turbocharger fan.
Custom Sheet Metal Fabrication.
10% off

Need custom metal and plastic parts?

Get 10% off your first order

No newsletter, no marketing, just a discount code for custom parts.

Thank you! Your submission has been received!
Oops! Something went wrong while submitting the form.

More resources

Technical Line Drawing

Get a quote in 24 hours

24 Hour Quote

Cookie Settings
By clicking “Accept”, you agree to the storing of cookies on your device to enhance site navigation, analyse site usage, and assist in our marketing efforts. View our Privacy Policy for more information.